3D Printing_OLA 3D Printing

OLA6200 ASA(BK)(FDM-PLASTIC)

More Details

OLA 6200 ASA (Black) is a rigid thermoplastic engineering material with mechanical properties similar to ABS. It is highly resistant to UV radiation and weathering, maintaining its color and shape even in harsh or prolonged sun exposure. This makes it ideal for printing outdoor-use parts and components.

Mechanical Properties
Tensile Strength (X-Y): 43-44.6 MPa
Tensile Strength (Z): 27.4 ± 1.8 MPa
Elongation at Break: 6.1% - 7.3%
Bending Strength: 73.4 ± 2.1 MPa
Thermal Properties
Heat Deflection Temperature: 105.3°C
Impact Properties
Notched Impact Strength: 10.3 ± 0.4 kJ/m²

Max. Part Size:

250mm x 250mm x 250mm

Tolerance and Precision：

±300 µm or ±0.3%

View Data Sheet

OLA7500 H-perform(MJF-Nylon)

3D Printing MJF Nylon Black

More Details

OLA 7500 is a high-performance PA12 material optimized for MJF printing technology. It provides outstanding part quality with exceptional surface detail and dimensional accuracy, making it ideal for intricate components and complex assemblies. A preferred choice for internal structures, housings, connectors, and functional parts requiring precision.

Mechanical Properties
Tensile Strength: 48 MPa
Tensile Modulus: 1800 MPa
Elongation at Break: 15-20%
Bending Strength: 70 MPa
Bending Modulus: 1800 MPa
Shore Hardness: 80
Notched Impact Strength: 3.5-3.6 kJ/㎡
Thermal Properties
Heat Deflection Temperature: 155°C
Melting Point: 187°C

Max. Part Size:

377mm x 277mm x 380mm

Tolerance and Precision：

±300 µm or ±0.3%

View Data Sheet

OLA8200(SLA-RESIN)

3D Printing SLA Resin Beige

More Details

As our most popular economy-grade material, OLA 8200 resin delivers outstanding surface finish and remarkable toughness, making it ideal for cost-sensitive rapid prototyping and pre-production verification.

Thermal Properties
Heat Deflection Temperature: 39–52°C
Glass Transition Temperature: 40–57°C
Coefficient of Thermal Expansion: 90–103×10⁻⁶/°C
Mechanical Properties
Tensile Modulus: 2589–2695 MPa
Tensile Strength: 38–56 MPa
Elongation at Break: 12–20%
Flexural Modulus: 2692–2775 MPa
Flexural Strength: 69–74 MPa
Notched Impact Strength: 35–55 J/m
Hardness (Shore D): 76–88
Poisson's Ratio: 0.4–0.44
Electrical & Physical Properties
Dielectric Constant (60Hz): 4.2–5.0
Dielectric Constant (1kHz): 3.3–4.2
Dielectric Constant (1MHz): 3.2–4.0
Dielectric Strength: 12.8–16.1 kV/mm
Density: 1.12–1.18 g/cm³

Max. Part Size:

1600mm x 750mm x 600mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

OLA-AlSi10Mg (SLM)

SLM AlSi10Mg Natural (Metallic Gray)

More Details

AlSi10Mg is a lightweight aluminum alloy with excellent strength-to-weight ratio, good thermal conductivity, and reliable mechanical properties. Known for its low density and great cost-effectiveness, this alloy is ideal for complex geometries, heat-resistant parts, and functional prototypes in aerospace, automotive, and electronics.

Surface Characteristics
Surface Roughness: ≥7 μm
Flame Resistance: V0
As-Printed State
Hardness: 69±3 HRB
Tensile Strength: 440±50 MPa
Yield Strength: 240±50 MPa
Elongation: 6±3%
Tensile Modulus: 2200-2770 MPa
Flexural Strength: 77-144 MPa
After Heat Treatment
Hardness: 63±3 HRB
Tensile Strength: 320±50 MPa
Yield Strength: 210±50 MPa
Elongation: 8±3%
Heat Deflection Temp: 216°C
Flexural Modulus: 2230-2820 MPa

Max. Part Size:

427mm × 527mm × 460mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

OLA 17-4PH（SLM）

17-4 SLM Natural (Metallic Grey)

More Details

17-4PH is a precipitation-hardened stainless steel known for its excellent corrosion resistance, high tensile strength at room temperature, and good weldability. It is widely used in tire mold manufacturing, medical applications, and various industrial tooling scenarios.

As-Printed State
Surface roughness (sandblasted): ≥6 μm
Hardness: HRB 94±3
Tensile strength: 900±100 MPa
Yield strength: 560±100 MPa
Elongation: 28±2%
Post-Heat Treatment
Hardness: HRB 41±3
Tensile strength: 1300±100 MPa
Yield strength: 1100±100 MPa
Elongation: 16±2%
Key Notes
"As-printed" refers to direct metal laser sintered (DMLS) state
H900 heat treatment condition shown (solution annealed + aged)
Hardness converts to ~HRC 38 as-printed / HRC 22 post-treatment

Max. Part Size:

320mm × 360mm × 360mm

Tolerance and Precision：

±200μm or ±0.2%

View Data Sheet

OLA Micronano ST Resin(LCD-RESIN)

3D pronting DLP Resin Black

More Details

Combines high strength and excellent toughness with ultra-precision DLP printing. Capable of printing fine structures down to 50μm with machining tolerances up to ±30μm. Offers superior surface quality and dimensional accuracy, making it ideal for precision engineering.

Mechanical Properties
Tensile Strength: 45 MPa
Elongation at Break: 15%
Bending Strength: 54 MPa
Bending Modulus: 1500 MPa
Hardness (Shore D): 75
Thermal Properties
Heat Deflection Temperature: 80°C
Other Properties
Viscosity: 800 cps

Max. Part Size:

84mm x 63mm x 70mm

Tolerance and Precision：

±30 µm or ±0.03%

View Data Sheet

Acrylonitrile Butadiene Styrene(Vacuum Casting-ABS)

Vacuum Casting White Black

More Details

A low-viscosity, easy-to-use polyurethane resin with excellent mechanical properties, ideal for prototypes similar to ABS thermoplastics.

Mechanical Properties
Tensile Strength: 50 MPa
Flexural Strength: 75 MPa
Flexural Modulus: 1800 MPa
Impact Strength: 60 kJ/m²
Shore Hardness (A): 78
Linear Shrinkage: 2%
Thermal Properties
Glass Transition Temperature: 85°C
Other Properties
Maximum Casting Thickness: 10 mm
Full Curing Time (23°C): 4 days

Max. Part Size:

900mm x 650mm x 600mm

Tolerance and Precision：

±500 µm or ±0.5%

View Data Sheet

OLA9085(FDM-PLASTIC)

3D Printing FDM Plastic Natural (light brown tone)

More Details

OLA 9085 is an amorphous thermoplastic with an outstanding strength-to-weight ratio and excellent FST (Flame, Smoke, Toxicity) ratings. Due to its existing certifications and superior performance under demanding conditions, it is ideal for aerospace, automotive, and military applications.

Flame Resistance
Flammability Rating: V0
Thermal Properties
Heat Deflection Temperature (HDT): 216°C
Mechanical Properties
Tensile Modulus: 2200-2770 MPa
Tensile Strength: 48-81 MPa
Elongation at Break: 2-3.3%
Flexural Strength: 77-144 MPa
Flexural Modulus: 2230-2820 MPa

Max. Part Size:

914mm x 610mm x 914mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

OLA6130 Nylon PA6 Carbon-Fiber Reinforced(SLS-NYLON)

3D Printing SLS Nylon Black

More Details

OLA 6130 PA6+CF is a carbon fiber–reinforced nylon material that delivers superior strength, stiffness, and heat resistance. Engineered for high-performance applications, it can replace traditional aluminum alloys and is suitable for complex load-bearing structures. Ideal for functional testing, small-batch production, and parts traditionally made via CNC or injection molding.

Thermal Properties
Heat Deflection Temperature (HDT @ 1.8 MPa): 210°C
Heat Deflection Temperature (HDT @ 0.45 MPa): 214°C
Mechanical Properties
Tensile Modulus (ISO 527-1:2019): 10000 MPa
Tensile Strength (ISO 527-1:2019): 110 MPa
Elongation at Break (ISO 527-1:2018): 2.5%
Bending Modulus (ISO 178:2019): 6000 MPa
Bending Strength (ISO 178:2019): 135 MPa
Impact Properties
Notched Impact Strength (ISO 180:2019): 4 kJ/m²
Unnotched Impact Strength (ISO 180:2019): 25 kJ/m²

Max. Part Size:

335mm x 335mm x 400mm

Tolerance and Precision：

±300 µm or ±0.3%

View Data Sheet

OLA8100(SLA-RESIN)

3D Printing SLA Resin White

More Details

OLA 8100 resin combines precision with outstanding mechanical and thermal properties, making it ideal for functional verification under mechanical stress and temperature variations.

Thermal Properties
Heat Deflection Temperature: 60°C
Mechanical Properties
Elongation at Break: 11%
Shore Hardness: 82
Tensile Strength: 56 MPa
Elastic Modulus: 2654 MPa
Tensile Modulus: 2964 MPa
Notched Impact Strength: 38.9 J/m
Water Absorption: 0.4%
Electrical Properties
Dielectric Constant (60 Hz): 3.9
Dielectric Constant (1 kHz): 3.7
Dielectric Strength: 31 kV/mm

Max. Part Size:

600mm x 600mm x 400mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

Polyamide(Vacuum Casting-PA)

Vacuum Casting White Black High stability

More Details

A transparent, easy-to-process, easy-to-demold, low-shrinkage polyurethane resin with mechanical properties similar to nylon.

Thermal Properties
Heat Deflection Temperature (HDT @ 1.8 MPa): 65°C - 110°C
Mechanical Properties
Tensile Strength (ISO527-1:2019): 60 MPa - 68 MPa
Tensile Modulus (ISO527-1:2019): Not Provided
Elongation at Break (ISO527-1:2018): 2% - 15%
Bending Strength (GB/T 9341-2008): 80 MPa - 88 MPa
Bending Modulus (GB/T 9341-2008): 2000 MPa - 3300 MPa
Impact Properties and Other Properties
Impact Strength (GB/T 1843-2008): 7 kJ/m² - 14 kJ/m²
Linear Shrinkage: 0.3% (mm/m)
Hardness (Shore D): 84 - 87
Maximum Pouring Thickness: 5 mm

Max. Part Size:

900mm x 650mm x 600mm

Tolerance and Precision：

±500 µm or ±0.5%

View Data Sheet

OLA1010(FDM-PLASTIC)

3D Printing FDM Plastic Natural (light brown tint)

More Details

OLA 1010 is one of the few thermoplastic resins approved for commercial aerospace applications. It is an amorphous engineering plastic known for its robustness, flame resistance, and stability under extreme temperatures.

Mechanical Properties
Tensile Modulus: 2200-2770 MPa
Tensile Strength: 48-81 MPa
Elongation at Break: 2-3.3%
Bending Strength: 77-144 MPa
Bending Modulus: 2230-2820 MPa
Thermal Properties
Heat Deflection Temperature: 216°C
Flame Retardancy
Flame Retardant Rating: V0

Max. Part Size:

914mm x 610mm x 914mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

OLAPA6 Glass-Fiber Reinforced(SLS-NYLON)

3D Printing SLS Nylon Gray-black

More Details

OLA PA6+GF is a high-performance, glass fiber–reinforced polyamide material known for its outstanding mechanical properties, high heat resistance, and excellent chemical stability. With superior strength and stiffness, it is capable of withstanding heavy loads and impacts, making it ideal for demanding industrial applications.

Thermal Properties
Heat Deflection Temperature: 203°C
Heat Deflection Temperature: 219°C
Mechanical Properties
Tensile Modulus: 6585 MPa
Tensile Strength: 77 MPa
Elongation at Break: 1.7%
Bending Modulus: 6066 MPa
Bending Strength: 130 MPa
Impact Properties
Notched Impact Strength: 4.2 KJ/m²
Unnotched Impact Strength: 13.6 KJ/m²

Max. Part Size:

350mm x 350mm x 400mm

Tolerance and Precision：

±400 µm or ±0.4%

View Data Sheet

OLA8000（SLA-RESIN）

3D Printing SLA Resin White

More Details

Using SLA stereolithography, this material offers high-precision, smooth-surfaced prints with moisture resistance. Certified for medical applications (USP Class VI, ISO10993), it's suitable for auxiliary tools. Supports post-processing but has limited strength and toughness.

Thermal Properties
Heat Deflection Temperature: 46°C
Water Absorption: 0.4%
Mechanical Properties
Shore Hardness: 79
Tensile Strength: 35 MPa
Elongation at Break: 6 - 9%
Elastic Modulus: 2370 - 2650 MPa
Flexural Strength: 67 MPa
Flexural Modulus: 2178 - 2222 MPa
Notched Impact Strength: 23 - 29 J/m
Poisson's Ratio: 0.41
Electrical Properties
Dielectric Constant (60Hz): 3.8
Dielectric Constant (1kHz): 3.7
Dielectric Constant (1MHz): 3.4
Dielectric Strength: 17.9 kV/mm

Max. Part Size:

600mm x 600mm x 400mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

OLA-TC-4 (SLM)

TC-4 SLM Natural (Silver-Grey)

More Details

Titanium alloy TC4, also known as Ti6Al4V, is a medium-strength α-β phase titanium alloy with excellent mechanical properties, biocompatibility, and corrosion resistance. It is widely used in the aerospace, medical, and chemical industries.

As-Printed State
Surface roughness (sandblasted) ≥7μm
Hardness: HRC 38±3
Yield strength: 1050±50 MPa
Elongation: 7±3%
Tensile strength: 1230±50 MPa
Post-Heat Treatment
Hardness: HRC 35±3
Yield strength: 950±50 MPa
Elongation: 13±3%
Tensile strength: 1015±50 MPa
Key Notes
"As-printed" emphasizes the raw manufactured state.
"Post-heat treatment" replaces "heat-treated" for technical accuracy.
Units follow ISO/ASTM standards (e.g., MPa not Mpa).

Max. Part Size:

350mm x 400mm x 360mm

Tolerance and Precision：

±200μm or ±0.2%

View Data Sheet

OLA Nylon Carbon Fiber(FDM-PLASTIC)

3D Printing FDM Plastic Black

More Details

Nylon carbon fiber is an advanced composite material combining nylon resin with carbon fiber particles. It retains the inherent advantages of nylon—chemical and corrosion resistance—while significantly enhancing mechanical strength and heat resistance.

Thermal Properties
Heat Deflection Temperature: 143 °C
Mechanical Properties
Tensile Modulus: 2300–7515 MPa
Tensile Strength: 34.4–75.6 MPa
Elongation at Break: 1.2–1.9 %
Flexural Strength: 58.1–142 MPa
Flexural Modulus: 1830–10620 MPa
Notched Impact Strength: 21.4–85 J/m

Max. Part Size:

914mm x 610mm x 914mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

Polycarbonate(Vacuum Casting-PC)

Vacuum Casting White Full-transparent&translucent Black

More Details

A transparent, easy-to-process, easy-to-demold, low-shrinkage polyurethane resin with mechanical properties similar to polycarbonate (PC)

Mechanical Properties
Tensile Strength: 55 MPa
Flexural Modulus: 1500 MPa
Flexural Strength: 90 MPa
Shore Hardness: 78
Linear Shrinkage: 3 mm/m
Elongation at Break: 16%
Maximum Casting Thickness: 5 mm
Full Curing Time (at 23°C): 4 days
Thermal Properties
Heat Deflection Temperature: 50–60°C
Impact Properties
Impact Strength: 50 kJ/m²

Max. Part Size:

900mm x 650mm x 600mm

Tolerance and Precision：

±500 µm or ±0.5%

View Data Sheet

OLA8228(SLA-RESIN)

3D Printing SLA Resin Light Green

More Details

OLA 8228 resin is a premium photopolymer resin offering exceptional hardness, accuracy and heat resistance, widely used for industrial functional and cosmetic verification.

Thermal and Physical Properties
Heat Deflection Temperature: 56.4℃
Mechanical Properties
Shore Hardness: 83
Water Absorption: 0.44
Tensile Modulus: 3200MPa
Tensile Strength: 62.4MPa
Flexural Strength: 83.1MPa
Flexural Modulus: 2390MPa
Elongation at Break: 16%

Max. Part Size:

600mm x 600mm x 400mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet

Polypropylene(Vacuum Casting-PP)

Vacuum Casting White Black

More Details

A vacuum casting material developed for producing PE and PP-like prototypes. It delivers a tactile feel and appearance similar to PE/PP parts.

Mechanical Properties
Tensile Strength: 34 MPa
Elongation at Break: 72%
Flexural Strength: 39 MPa
Flexural Modulus (Young's Modulus): 960 MPa
Impact Strength: 10 kJ/m²
Shore Hardness: 76
Thermal Properties
Heat Deflection Temperature: 70°C
Dimensional Properties
Linear Shrinkage: 3 mm/m

Max. Part Size:

900mm x 650mm x 600mm

Tolerance and Precision：

±500 µm or ±0.5%

View Data Sheet

OLA ABS(FDM-PLASTIC)

3D Printing FDM Plastic Black

More Details

Engineering thermoplastic, High strength, Injection-molding-like quality
Engineering-grade thermoplastic with injection-molding comparable performance

Soluble support enables complex internal structures and piping parts

Combines high strength with precision for consistent production

Mechanical Properties
Tensile Strength: 28-32 MPa
Tensile Modulus: 2180-2230 MPa
Elongation at Break: 2-7%
Bending Strength: 48-60 MPa
Bending Modulus: 1760-2060 MPa
Notched Impact Strength: 128-300 J/m²
Thermal Properties
Heat Deflection Temperature (HDT): 82-96°C
Flammability: HB

Max. Part Size:

1000mm x 610mm x 610mm

Tolerance and Precision：

±200 µm or ±0.2%

View Data Sheet