OLA 6130 PA6+CF is a carbon fiber–reinforced nylon material that delivers superior strength, stiffness, and heat resistance. Engineered for high-performance applications, it can replace traditional aluminum alloys and is suitable for complex load-bearing structures. Ideal for functional testing, small-batch production, and parts traditionally made via CNC or injection molding.
Thermal Properties
Heat Deflection Temperature (HDT @ 1.8 MPa): 210°C
Heat Deflection Temperature (HDT @ 0.45 MPa): 214°C
Mechanical Properties
Tensile Modulus (ISO 527-1:2019): 10000 MPa
Tensile Strength (ISO 527-1:2019): 110 MPa
Elongation at Break (ISO 527-1:2018): 2.5%
Bending Modulus (ISO 178:2019): 6000 MPa
Bending Strength (ISO 178:2019): 135 MPa
Impact Properties
Notched Impact Strength (ISO 180:2019): 4 kJ/m²
Unnotched Impact Strength (ISO 180:2019): 25 kJ/m²
Max. Part Size:
335mm x 335mm x 400mm
Tolerance and Precision：
±300 µm or ±0.3%